當(dāng)前位置：上海巨納科技有限公司>>二維材料>>二維材料薄膜>>基于藍(lán)寶石襯底的全區(qū)域覆蓋的單層二硒化錸

基于藍(lán)寶石襯底的全區(qū)域覆蓋的單層二硒化錸

返回列表頁

參考價

面議

具體成交價以合同協(xié)議為準(zhǔn)

產(chǎn)品型號

品牌

廠商性質(zhì)其他

所在地上海

在線詢價收藏產(chǎn)品查看聯(lián)系電話

聯(lián)系方式：袁文軍查看聯(lián)系方式

更新時間：2024-02-15 14:52:37瀏覽次數(shù)：105次

聯(lián)系我時，請告知來自環(huán)保在線

產(chǎn)品分類 品牌分類

  二維材料

二維材料粉末

二維材料溶液

碲化物晶體

硒化物晶體

硫化物晶體

絕緣體

鈣鈦礦

異質(zhì)結(jié)

MOFS材料

二維材料薄膜

黑磷

六方氮化硼

其他二維材料

全部產(chǎn)品列表

暫無信息

上海巨納科技有限公司

經(jīng)營模式：其他

商鋪產(chǎn)品：574條

所在地區(qū)：

聯(lián)系人：袁文軍

詢價 給他留言

產(chǎn)品簡介

簡要描述：This product contains full area coverage ReSe2 monolayers on c-cut sapphire substrates.

詳細(xì)介紹

This product contains full area coverage ReSe2 monolayers on c-cut sapphire substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick ReSe2 sheet. Synthesized full area coverage monolayer ReSe2 is highly crystalline, some regions also display significant crystalline anisotropy.

Sample Properties.

Sample size	1cm x 1cm square shaped
Substrate type	Sapphire c-cut (0001)
Coverage	Full monolayer coverage
Electrical properties	1.45 eV Anisotropic Semiconductor (Indirect Bandgap)
Crystal structure	Distorted Tetragonal Phase (1T’)
Unit cell parameters	a = 0.656 nm, b = 0.672 nm, c = 0.674 nm, α = 91.74°, β = 105°, γ = 119°
Production method	Atmospheric Pressure Chemical Vapor Deposition (APCVD)
Characterization methods	Raman, angle resolved Raman spectroscopy, photoluminescence, absorption spectroscopy TEM, EDS

Specifications

ReSe2 monolayers do not contain intentional dopants or defects. However, our technical staff can produce defected ReSe2 using α-bombardment technique.

Supporting datasets [for 99% Full area ReSe2 monolayers on c-cut Sapphire]

Transmission electron images (TEM) and angle resolved Raman spectroscopy measurements acquired from CVD grown full area coverage ReSe2 monolayers on c-cut sapphire confirming crystalline anisotropy

Energy dispersive X-ray spectroscopy (EDX) characterization on CVD grown full area coverage monolayer ReSe2 on c-cut sapphire

Raman spectroscopy measurement confirm monolayer nature of the CVD grown samples. Differential reflectance measurements clearly show bａnd gap at 1.45 eV for monolayer ReS2 consistent with the existing literature values. PL spectrum does not show any PL signal due to indirect bａnd nature.